Effects of Nb on Creep Properties and Hot Corrosion Resistance of New Alumina-Forming Austenitic Steels at 700 °C

Abstract

Effects of Nb on the creep resistance and hot corrosion behavior of the Fe-25Cr-35Ni-2.5Al-xNb (x = 0, 0.6, 1.2) Alumina-Forming Austenitic stainless steels (AFA steels) at 700 °C were investigated. The addition of Nb promoted the precipitation of both nanoscale NbC and γ′-Ni3(Al, Nb) phases, which exhibited very low coarsening rate constants. The nanoscale NbC and γ′-Ni3(Al, Nb) phases effectively impeded the migration of dislocations and led to an improvement in creep performance of the Nb-addition AFA steel. The corrosion of AFA steels in Na2SO4-25%K2SO4 at 700 °C was primarily driven by an “oxidation-sulfidation” mechanism. The addition of Nb, serving as a third element, facilitated the formation of protective Cr2O3 and Al2O3 films, which improved the hot corrosion resistance performance. However, the formation Nb2O5 was found to compromise the compactness of the oxide film, which adversely affected the corrosion resistance.

Keywords

• Alumina-Forming Austenitic steel (AFA)
• Nb addition
• creep properties
• hot corrosion