Co-Precipitation Synthesized Ag-Doped Ceria Redox Material (ACRM) for the Thermochemical Conversion of CO₂ into Solar Fuels

Abstract

In this investigation, an effort was made to introduce Ag into the CeO2 fluorite crystal lattice to form Ce0.99Ag0.01O2-δ (ACRM) using an ammonium hydroxide-assisted co-precipitation method. The resulting powder obtained after the co-precipitation reaction, filtration, and drying was annealed at 800 °C in a muffle furnace to obtain crystalline ACRM. The phase composition and microstructure of the synthesized ACRM were analyzed using a powder X-ray diffractometer (PXRD) and a scanning electron microscope (SEM). The characterized ACRM powder was then subjected to multiple thermochemical thermal reduction (TR) and CO2 splitting (CDS) cycles using a high-temperature thermogravimetric analyzer (TGA). The TR step was conducted using Ar gas as an inert atmosphere, maintaining the temperature at 1400 °C for 60 min. Subsequently, the same powder was subjected to the CDS step by treating it with a gaseous mixture of 50% CO2 and Ar gas at 1000 °C for 30 min. ACRM displayed stable redox reactivity towards thermochemical CDS cycles by generating an average of 50.9 μmol of O2/g·cycle and 101.6 μmol of CO/g·cycle, respectively, over 10 thermochemical cycles.

Keywords

• ceria
• CO₂ splitting
• thermochemical
• TGA
• Co-precipitation
• solar energy