Microplastic-Related Leachate from Recycled Rubber Tiles: The Role of TiO₂ Protective Coating

Abstract

The extensive global use of rubber results in significant microplastic pollution from the release of tire wear particles and microplastic leachate, impacting the environment, human health, and ecosystems. Waste tires are normally recycled and used for the production of new products, such as rubber tiles. The presented study aims to show the possibility of further decrease in the negative environmental impact of materials based on recycled rubber. This paper presents the modification of rubber tiles with a titanium dioxide (TiO2) coating, focusing on surface integrity, rubber particle wear release, and the consequent environmental impact of leachate release. Both reference and modified rubber tiles were subjected to artificial accelerated aging in a solar simulator for 4, 6, and 8 weeks, followed by an abrasion test. The carbonyl index was calculated from FTIR characterization after each time frame to indicate the degradation of organic compounds and chemical changes caused by UV exposure. A 24 h leaching test with a liquid-to-sample ratio of 1:20 was performed on both rubber tile samples prior to and after 8 weeks of aging along with the aged wear particles for the purpose of the non-target screening of released organic leachate by LC/MS QTOF. The results of carbonyl indices showed that the TiO2 coating contributes to the stabilization of polymer degradation and, to a certain extent, reduces the leaching of organic compounds, such as phthalates. However, the increased wear and release of rubber particles and the subsequent degradation of organic leachates require further in-depth research.

Keywords

• waste tires
• rubber tiles
• titanium dioxide
• surface aging
• microplastics leachate