Preparation of a Flexible X-Band Radar-Wave-Absorbing Composite Material by Using Beta-Silicon Carbide and Polyurethane as Substrates and Multiwalled Carbon Nanotubes as Additives

Abstract

Silicon carbide (SiC) has good chemical resistance, excellent mechanical properties, thermal conductivity, especially in extreme conditions of application, and has proved to be a very promising electromagnetic absorption material. However, single silicon carbide cannot meet the increasing demand for high performance of absorbing materials. It has become an important research direction to combine it with other absorbing materials to improve its absorbing performance. In this study, a composite absorber material was prepared by 50 wt.% micron-sized beta-silicon carbide (β-sic) powder, mixed with a 0.2 wt.% multiwalled carbon nanotubes (MWCNTs) and 50 wt.% polyurethane (PU) substrate. The mixture was stirred and deaerated to form a slurry, and sprayed onto synthetic fabric. The results showed that the composite material was flexible, with a thickness of less than 2 mm and favorable adhesion. The results obtained by reflection graph of the radar waves, indicated that the return loss within the X-band range (8–12 GHz) was less than −40 dB, indicating favorable radar wave absorption. Therefore, composite materials could thus be used successfully as radar wave absorbers, and was suitable for stealth materials in “asymmetric warfare”.

Keywords

• beta-silicon carbide (β-SiC)
• composite absorber material
• multiwalled carbon nanotube
• polyurethane
• return loss
• X-band