Processing and Evaluation of a Carbon Fiber Reinforced Composite Bar Using a Closed Impregnation Pultrusion System with Improved Production Speed

Abstract

In this paper, an epoxy resin-based carbon fiber reinforced composite (CFRP) bar pultrusion system using a closed impregnation device which has various advantages in process compared to traditional open bath type pultrusion system was developed, and the fiber impregnation system was improved through the analysis of resin properties for the high-speed production of CFRP bars used to support the mother glass in the display transfer cassettes. To improve the fiber feeder system, fiber guides were switched from perforated plates to roller guides for spreading fibers, which allowed the input fibers to be widened and flattened while reducing the fiber thickness. Additionally, the correlation between resin viscosity and impregnation speed were analyzed to evaluate the resulting mechanical properties at different pultrusion speeds and temperatures. A CFRP bar was produced with resin injection at room temperature and a pultrusion rate of 400 mm/min and compared to a CFRP bar produced with fiber spreading, a resin injection temperature of 40 °C, and a pultrusion rate of 600 mm/min; the latter with a 50% improved production rate showed improvements in mechanical properties, including the cross-sectional void by 98.7%, surface roughness by 75.5%, deflection by 34.9%, and bending strength by 70%.

Keywords

• pultrusion
• carbon fiber reinforced composite (CFRP)
• fiber spreading
• Darcy’s law