Surface Stoichiometry and Depth Profile of Ti_<i>x</i>-Cu_<i>y</i>N_<i>z</i> Thin Films Deposited by Magnetron Sputtering

Abstract

We report the surface stoichiometry of Tix-CuyNz thin film as a function of film depth. Films are deposited by high power impulse (HiPIMS) and DC magnetron sputtering (DCMS). The composition of Ti, Cu, and N in the deposited film is investigated by X-ray photoelectron spectroscopy (XPS). At a larger depth, the relative composition of Cu and Ti in the film is increased compared to the surface. The amount of adventitious carbon which is present on the film surface strongly decreases with film depth. Deposited films also contain a significant amount of oxygen whose origin is not fully clear. Grazing incidence X-ray diffraction (GIXD) shows a Cu3N phase on the surface, while transmission electron microscopy (TEM) indicates a polycrystalline structure and the presence of a Ti3CuN phase.

Keywords

• magnetron sputtering
• Ti-Cu-N coating
• N incorporation
• X-ray photoelectron spectroscopy
• X-ray diffraction
• Transmission electron microscopy