Improvement of the technological process of manufacturing bearing grades of steel at the 370/150 mill.

Abstract

The actual problem of obtaining long products from bearing steel grades with specified microstructure characteristics is considered. The analysis of the capabilities of the existing equipment – a heating furnace and a rolling mill 370/150 of OJSC “BSW – Management Company of the Holding “BMC” was carried out in order to introduce technical measures aimed at reducing carbide heterogeneity in products made of bearing steel grades on the example of steel grade 100Cr6.The influence of different modes of preliminary thermal preparation of continuously cast billets from bearing steel grades on the carbide inhomogeneity in the finished rolling is studied. According to the results of the research, the optimal mode of heat treatment of a continuously cast billet was determined, which allows to produce rolled products that meet the highest requirements of consumers.

Keywords

• bearing steel
• continuously cast billet
• rolling temperature mode
• rolling deformation mode
• steel microstructure defects
• carbide inhomogeneity(segregation)
• modeling