Enhanced Leaching of Zinc from Zinc-Containing Metallurgical Residues via Microwave Calcium Activation Pretreatment

Abstract

Given the shortage of zinc resource, the low utilisation efficiency of secondary zinc resource, and the crucial problem that the synchronous dissolution of zinc from different mineral phases, an activation pretreatment method merged with calcium activation and microwave heating approach was proposed to enhance the zinc leaching from complex encapsulated zinc-containing metallurgical residues (ZMR). Results indicated that under the optimal pretreatment conditions, including microwave activation temperature of 400 °C, CaO addition of 25% and activation time of 20 min, the zinc leaching rate reached 91.67%, which was 3.9% higher than that by conventional roasting pretreatment. Meanwhile, microwave heating presents excellent treatment effects, manifested by the zinc leaching rates, all exceeding that of conventional roasting under the same conditions, while the process temperature is decreased by 200 °C. In addition, XRD and SEM-EDS analysis denoted that microwave calcification pretreatment can effectively promote the transformation of the refractory zinc minerals like Zn2SiO4 and ZnFe2O4 into the easily leachable zinc oxides. The distinctive selective heating characteristics of microwave heating strengthened the dissociation of mineral inclusion, and the generated cracks increased the interfacial reaction area and further enhancing the leaching reaction of zinc from ZMR.

Keywords

• zinc-containing metallurgical residues
• calcium activation
• microwave heating
• enhanced leaching