Metals (Feb 2021)
Flow Field in Slab Continuous Casting Mold with Large Width Optimized with High Temperature Quantitative Measurement and Numerical Calculation
Abstract
In this paper, the rod deflection method was applied to quantitatively measure velocity near the mold surface at high temperatures and the k-ε model coupled with a discrete phase model (DPM) was adopted to simulate the flow field in the mold. The calculated results match very well with the measured results under all the present conditions. Under the conditions of the large mold width of 1800 mm, 1.1 m/min casting speed and 140 mm submerged entry nozzle (SEN) immersion depth, the velocity near the mold surface decreases with increasing the argon gas flow rate. When the argon gas flow rate is 6 L/min, the flow pattern is the double roll flow (DRF). When the argon gas flow rate is increased to 10 L/min and 14 L/min, the flow pattern is the single roll flow (SRF), and the risk of slag entrainment increases. With an argon gas flow rate of 10 L/min, and an immersion depth of 160 mm, the velocity near the mold surface sensitively increases with increasing the casting speed. When the casting speed is 1.1 m/min, an intermediate flow (IF) is formed with the intensified mold surface fluctuation, which can easily result in slag entrainment defects. When the casting speed is only increased to 1.2 m/min, the velocity near the mold surface changes drastically and is close to the upper limit velocity of 0.4 m/s. When the casting speed is 1.1 m/min, and the argon gas flow rate is 10 L/min, the velocity near the mold surface is obviously increased with increasing the immersion depth. When the immersion depth of the nozzle increases from 140 mm and 160 mm to 180 mm, the flow pattern changes from SRF or IF to DRF. When the bottom shape of the SEN changes from mountain to well, the velocity near the mold surface decreases. We suggest adopting the well-bottom nozzle to reduce the risk of slag entrainment.
Keywords