Effect of Electrolyte Temperature on Plasma Electrolytic Oxidation of Pure Aluminum

Abstract

Plasma electrolytic oxidation (PEO) is normally carried out under conditions with electrolyte cooling. However, the effect of the temperature of the electrolytes on the PEO behavior and properties of the resulting coatings is seldom investigated. In this study, PEO of pure Al was carried out in a dilute aluminate electrolyte with the electrolyte temperature being controlled under low (~10–30 °C), medium (~40–50 °C) and high (~70–80 °C) temperature ranges, respectively. The morphology, microstructure, composition and phase component of the coatings fabricated under the different temperature ranges were analyzed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The corrosion resistances of the coatings were evaluated by electrochemical methods. The hardness of the coatings and substrate following the PEO treatment in the different electrolyte temperature ranges were also tested. It was found that a higher electrolyte temperature resulted in a higher growth rate and rougher coatings. Moreover, the α-Al2O3 content was reduced as the electrolyte temperature increased. The highest corrosion resistance was registered for the coating obtained under the lowest temperature range, whereas the corrosion resistance of the coating obtained under the highest temperature range was the worst. The higher growth rate under high electrolyte temperatures was associated with the increased kinetics of the PEO reactions. However, the temperature of the electrolyte should be controlled under a suitable range to ensure reasonable coating properties.

Keywords

• plasma electrolyte oxidation
• pure aluminum
• electrolyte temperature
• corrosion resistance