Influence of Storage Temperature on Orthodontic Elastics

Abstract

Introduction: Orthodontic elastics are a very significant tool in orthodontics, as it is the most commonly used force delivering unit. Temperature plays a key role in the amount of force that elastics are able to produce. Hence, there is a need to evaluate the influence of storage temperature on the properties of orthodontic elastics before its clinical use. Aim: To evaluate the influence of different storage temperature of latex orthodontic elastics. Materials and Methods: This cross-sectional study was conducted at Sathyabama Dental College and Hospital, Chennai, in November 2019. Sample of 40 latex orthodontic elastics (TP Orthodontics, medium force, standard size of 3/16′′) were divided into four groups with 10 elastics each, based on their storage temperature and stored in closed plastic packages. Group 1 was kept as a Control group and Group 2, Group 3 and Group 4 were stored in three Incubators under the specified storage temperatures such as 26-28°C, 4-8°C, 37°C respectively. The elastics were stretched and their forces measured in six progressive increases of 100% of their inner diameter, starting at a level of 100% stretching, with the Universal Testing Machine, Instron. The samples were also tested for Maximum Stress (MPa), Maximum Force (N), Maximum Elongation (%) and Break Distance (mm). Data were analysed using Statistical Package for the Social Science (SPSS) software version 16.0, one-way Analysis of Variance (ANOVA) and post-hoc test. Results: On evaluating the stress at 100%, 200%, 300%, 400%, 500%, 600% of strain, there was no statistically significant difference between the groups. Maximum Stress MPa was found to be 24.12±3.32, 25.12±3.42, 23.3±3.41, 23.97±3.50 for group1, group 2, group 3 and group 4 respectively. Maximum Elongation (%) was found to be 1369.0±25.108, 1364.0±23.190, 1359.0±35.103, 1363.0±34.657 for group 1, group 2, group 3 and group 4, respectively. Break Distance (mm) was found to be 68.48±1.267, 68.28±1.267, 67.87±1.77 and 68.19±1.727 for group1, group 2, group 3 and group 4, respectively. And none of the parameters tested showed statistical significance between the four groups. Conclusion: Latex elastics may be stored under any of the conditions tested in the present study over a period of one month, since different storage temperatures over a period of one month did not interfere in their mechanical properties.

Keywords

• break
• elongation
• stress
• strain