Evaluation of sealing efficacy and removal convenience of sealing materials for implant abutment screw access holes

Abstract

Abstract Background Sealing materials are used to fill abutment screw access holes (SAH) to prevent microleakage and protect the central screws in oral implant restoration. However, thus far, no consensus has been reached on sealing material selection. In this study, a comparison of the sealing efficacy and removal convenience of different sealing materials for cement-retained implant restoration was conducted. Methods Various sealing materials were classified into five groups, namely, gutta-percha (GP), temporary restorative paste (TRP), vinyl polysiloxane (VPS), polytetrafluoroethylene (PTFE) tape, and onlay resin (OR), and 35 sets of analog-abutments were allocated into five groups of seven specimens. A sealing efficacy test was conducted using a modified dye-penetration method, in which a lower absorbance indicated better sealing efficacy. For the removal-convenience test, the materials were removed from each SAH after solidification, and the retrieval time was recorded. Results On days 1 and 10, PTFE exhibited the highest absorbance value with significant differences compared to the other groups. On day 30, TRP and PTFE showed significantly higher absorbance values than GP, VPS, and OR, but no significant difference was detected between TRP and PTFE (p = 0.424). The absorbance values of TRP and PTFE from days 1, 10, and 30 showed significant intragroup differences, while those of the other groups did not. In terms of the removal convenience on days 1, 10, and 30, VPS achieved the best performance, followed by PTFE, OR, TRP, and GP. Conclusion Within the limitations of this experiment, VPS and OR showed better sealing efficacy against microleakage and a more convenient removal than the other materials; thus, VPS and OR are recommended for clinical use.

Keywords

• Oral implant
• Abutment
• Microleakage
• Sealing material
• Removal convenience
• Screw access hole