Dispersion and Lubrication of Zinc Stearate in Polypropylene/Sodium 4-[(4-chlorobenzoyl) amino] Benzoate Nucleating Agent Composite

Abstract

Zinc stearate (Znst) was physically blended with the sodium 4-[(4 chlorobenzoyl) amino] benzoate (SCAB) to obtain the SCAB-Znst composite nucleating agent. Znst was used to improve the dispersion property of SCAB and exert a lubricating effect on the PP matrix. The scanning electron microscopy and the fracture surface morphology of the PP/SCAB composite illustrated that the addition of Znst greatly reduced the aggregation phenomenon of SCAB in the PP matrix. The result of the rotary rheometer indicated that Znst exhibits internal lubrication in PP. The DSC result illustrated that the crystallization properties of PP were improved. Compared with pure PP, the Tc of the PP/SCAB composite increased by 1.44 °C (PP/Znst), 13.48 °C (PP/SCAB), and 14.96 °C (PP/SCAB-Znst), respectively. The flexural strength of pure PP, PP/SCAB, and PP/SCAB-Znst were 35.8 MPa, 38.8 MPa, and 40.6 MPa, respectively. The tensile strength of the PP/SCAB and PP/SCAB-Znst reached the values of 39.8 MPa and 42.9 MPa, respectively, compared with pure PP (34.1 MPa). The results demonstrated that Znst can promote the dispersion of SCAB in the PP matrix while exerting a lubricating effect, which enabled the enhancement of the crystalline and mechanical properties of PP.

Keywords

• sodium 4-[(4-chlorobenzoyl) amino] benzoate
• zinc stearate
• composite nucleating agent
• polypropylene