Ultrasound and Microwave-Assisted Synthesis of Hexagonally Ordered Ce-Promoted Mesoporous Silica as Ni Supports for Ethanol Steam Reforming

Abstract

Solvothermal synthesis of mesoporous materials based on amphiphilic molecules as structure-directing agents can be enhanced using non-conventional technologies for stirring and thermal activation. Here, we disclose a green synthesis approach for the preparation of cerium-modified hexagonally ordered silica sieves. Ultrasound micromixing enabled us to obtain well-dispersed Ce in the self-assembled silica network and yielded ordered materials with high cerium content (Ce/Si molar ratio = 0.08). Microwave dielectric heating, applied by an innovative open-end coaxial antenna, was used to reduce the overall hydrothermal synthesis time and to improve the surface area and textural properties. These mesoporous materials were used as a Ni catalyst support (10 wt.% metal loading) for the ethanol steam reforming reaction. The new catalysts featured complete ethanol conversion, high H2 selectivity (65%) and better stability, compared to the same catalyst prepared with magnetic stirring and conventional heating. The Ce-promoted silica sieves offered a suitable support for the controlled growth of nanocarbon that does not result in catalyst deactivation or poisoning after 6 h on stream.

Keywords

• Cerium catalyst
• green chemistry
• MCM-41
• mesoporous materials
• microwave chemistry
• nickel catalyst