Gentamicin Sulfate Grafted Magnetic GO Nanohybrids with Excellent Antibacterial Properties and Recyclability

Abstract

In this study, magnetic graphene oxide (MGO) nanohybrids were first prepared by loading Fe3O4 NPs onto graphene oxide (GO). Then, GS-MGO nanohybrids were prepared by grafting gentamicin sulfate (GS) onto MGO directly using a simple amidation reaction. The prepared GS-MGO had the same magnetism as MGO. They exhibited excellent antibacterial ability against Gram-negative bacteria and Gram-positive bacteria. The GS-MGO had excellent antibacterial performance against Escherichia coli (E. coli), Staphylococcus aureus (S. aureus), and Listeria monocytogenes (L. monocytogenes). When the addition concentration of GS-MGO was 1.25 mg/mL, the calculated bacteriostatic ratios against E. coli and S. aureus achieved 89.8% and 100%, respectively. For L. monocytogenes, only 0.05 mg/mL of GS-MGO had an antibacterial ratio as high as 99%. In addition, the prepared GS-MGO nanohybrids also exhibited excellent non-leaching activity with good recycling antibacterial ability. After eight times antibacterial tests, GS-MGO nanohybrids still exhibited an excellent inhibition effect on E. coli, S. aureus, and L. monocytogenes. Therefore, as a non-leaching antibacterial agent, the fabricated GS-MGO nanohybrid had dramatic antibacterial properties and also showed great recycling ability. Thus, it displayed great potential in the design of novel recycling antibacterial agents with non-leaching activity.

Keywords

• magnetic
• graphene oxide
• gentamicin sulfate
• antibacterial
• recyclable activity