Microstructure and tribological behavior of W-Mo alloy coating on powder metallurgy gears based on double glow plasma surface alloying technology

Wei D.-B.; Liang H.-X.; Li S.-Q.; Li F.-K.; Ding F.; Wang S.-Y.; Liu Z.-L.; Zhang P.-Z.

doi:10.2298/JMMB181031022D

Journal of Mining and Metallurgy. Section B: Metallurgy (Jan 2019)

Microstructure and tribological behavior of W-Mo alloy coating on powder metallurgy gears based on double glow plasma surface alloying technology

Wei D.-B.,
Liang H.-X.,
Li S.-Q.,
Li F.-K.,
Ding F.,
Wang S.-Y.,
Liu Z.-L.,
Zhang P.-Z.

Affiliations

Wei D.-B.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China + Key Laboratory of Materials Preparation and Protection for Harsh Environment (Nanjing University of Aeronautics and Astronautics), M
Liang H.-X.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China
Li S.-Q.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China
Li F.-K.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China
Ding F.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China
Wang S.-Y.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China + Key Laboratory of Materials Preparation and Protection for Harsh Environment (Nanjing University of Aeronautics and Astronautics), M
Liu Z.-L.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China
Zhang P.-Z.: Nanjing University of Aeronautics and Astronautics, College of Materials Science and Technology, Nanjing, Jiangsu, China + Key Laboratory of Materials Preparation and Protection for Harsh Environment (Nanjing University of Aeronautics and Astronautics), M

DOI: https://doi.org/10.2298/JMMB181031022D
Journal volume & issue: Vol. 55, no. 2
pp. 227 – 234

Abstract

Read online

In the present paper, plasma surface alloying was implemented on powder metallurgy gears to improve its wear resistance based on double glow plasma surface metallurgy technology. A W-Mo alloy coating was obtained in the process. The morphology, microstructure and phase composition were investigated by SEM, EDS and XRD. The hardness was examined by Vickers hardness test and nanoindentation test. The tribological behavior of powder metallurgy gears before and after plasma surface alloying was evaluated on a ball-on-disc reciprocating sliding tribometer under dry sliding condition at room temperature. The results indicate that the W-Mo alloy coating is homogeneous without defects, which includes deposition layer and interdiffusion layer. The average microhardness of powder metallurgy gears before and after plasma surface alloying is 145.8 HV0.1 and 344.4 HV0.1, respectively; Nano hardness of deposition layer and interdiffusion layer is 5.76 GPa, 14.35 GPa, respectively. The specific wear rate of W-Mo alloy coating is lower than original PM gears. The wear mechanism of W-Mo alloy coating is slight adhesive wear. The W-Mo alloy coating prepared by double glow plasma surface alloying technology can effectively improve wear resistance of powder metallurgy gears.

Published in Journal of Mining and Metallurgy. Section B: Metallurgy

ISSN: 1450-5339 (Print); 2217-7175 (Online)
Publisher: Technical Faculty, Bor
Country of publisher: Serbia
LCC subjects: Technology: Mining engineering. Metallurgy
Website: http://www.doiserbia.nb.rs/journal.aspx?issn=1450-5339

About the journal

Abstract

Keywords