Study of the Dielectric and Corona Resistance Properties of PI Films Modified with Fluorene Moiety/Aluminum Sec-Butoxide

Abstract

With the policy tilt and increased investment in research and development in the world, new energy vehicle technology continues to progress and the drive motor power density continues to improve, which puts forward higher requirements for the comprehensive performance of the core insulating material enameled wire enamel for drive motors. Polyimide (PI) has excellent electrical insulation properties, and heat resistance is often used to drive the motor winding insulation. To further improve the corona resistance and insulating properties of PI wire enamel varnish, in this paper, firstly, fluorene groups with a rigid conjugated structure were introduced into the molecular chain of the PI film by molecular structure modulation, and then uniformly dispersed alumina nanoclusters (AOCs) were introduced into the PI matrix by using an in situ growth process to inhibit the migration of high-energy electrons. The quantum size effect of the alumina nanoclusters was exploited to synergistically enhance the suppression and scattering of energetic moving electrons by PI-based composite films. The results show that the breakdown field strength of the PI-based composite film (MPI/1.0 vol% AOC) reaches 672.2 kV/mm, and the corona resistance life reaches 7.9 min, which are, respectively, 1.55 and 2.19 times higher than those of the initial PI film. A PI-based composite film with excellent insulating and corona resistance properties was obtained.

Keywords

• polyimide
• molecular structure control
• breakdown strength
• corona resistance