Experimental Investigation of Concrete Cylinders Confined with PBO FRCM Exposed to Elevated Temperatures

Abstract

Externally bonded fiber-reinforced polymers (FRPs) have been widely used for strengthening and retrofitting applications. However, their efficacy is hindered by the poor resistance of their epoxy resins to elevated temperatures and their limited compatibility with concrete substrates. To address these limitations, fabric-reinforced cementitious matrix (FRCM), also known as textile reinforced mortar (TRM), systems have emerged as an alternative solution. In this study, experimental tests were performed on concrete cylinders confined with FRCM systems that consisted of mineral mortar and poliparafenilenbenzobisoxazole fabric (PBO). The cylinders with concrete strengths of 30, 45, and 70 MPa, were confined with one or two FRCM layers, and were subjected to different target temperatures (100, 400, and 800 °C). The experimental results highlighted the confinement effect of FRCMs on the compressive strength of the tested cylinders. Cylinders exposed to 100 °C exhibited a slight increase in their compressive strength, while no specific trend was observed in the compressive strength of cylinders heated to 400 °C. Specimens heated up to 800 °C experienced a significant reduction in strength, reaching up to 82%.

Keywords

• composites
• confined concrete
• columns
• elevated temperatures
• fire
• FRCM