Synthesis and characterization of Pr substituted Gd-123 high-Tc superconductors Síntese e caracterização de supercondutores de alta temperatura crítica Gd1-xPr x-123, x=0/0,1/0,2/0,3

Abstract

High Tc superconducting materials with chemical formula Gd1-xPr xBa2Cu3O7-δ, where x = 0.0, 0.1, 0.2 and 0.3 were prepared by ceramic route. XRD studies confirm the orthorhombic pervoskite structure. Electrical resistivity measurement shows that Tc decreases with increasing Pr concentration. Copper valency and oxygen content decreasing with increasing Pr content. Value of n(CuO2) decreases with increasing x and oxygen deficiency (δ) has a linear dependence with (2x+δ). SQUID investigation reveals that Bohr magneton number and Curie constant are decreasing with increasing Pr concentration. Annihilation of superconductivity may be owing to reduction in CuO2 charge carriers or magnetic pair breaking.Materiais supercondutores de alta temperatura crítica com fórmula química Gd1-xPr xBa2Cu3O7-δ, x = 0/0,1/0,2/0,3 foram preparados pela rota cerâmica. Estudos de difração de raios X confirmam a estrutura perovskita ortorrômbica. Medidas de resistividade elétrica mostram que T C diminui com o aumento da concentração de Pr. A valência do cobre e o teor de oxigênio diminuem com o aumento do teor de praseodímio. O valor de n(CuO2) diminui com o aumento de x e a deficiência de oxigênio δ tem uma dependência linear com (2x+δ). Pesquisas em SQUID revelam qu o número do magneton de Bohr e a constante de Curie diminuem com o aumento da concentração de praseodímio. A aniquilação da supercondutividade pode ser devida à redução de portadores de carga em CuO2 ou quebra magnética dos pares.

Keywords

• Gd-123 HTSC
• teor de oxigênio
• resistividade elétrica
• lei de Curie-Weiss
• Gd-123 HTSC
• oxygen content
• electrical resistivity
• Curie - Weiss law