Investigation of Fluidity and Strength of Enhanced Foam-Cemented Paste Backfill

Abstract

To solve the problems of high cement dosage and poor fluidity of conventional cemented paste backfill (CPB) materials, the fluidity and strength properties of foam-cemented paste backfill (FCPB) were studied in combination. Based on determining the optimum contents of a foaming agent and a foam stabilizer, FCPB density was measured. To investigate the fluidity and strength of FCPB under different foam contents (0%, 5%, 10%, 15%, 20%, 25%, 30%, and 40%), different solid contents (75 wt.% and 77 wt.%), and different cement-tailing ratios (1:4 and 1:5), spread tests and unconfined compressive strength (UCS) tests were conducted. In addition, the FCPB microstructure was analyzed by scanning electron microscopy (SEM). The results indicate that the optimum combination dosages of sodium lauryl sulfate (K12) and sodium carboxymethyl cellulose (CMC) are 0.5 g/L and 0.2 g/L. The density decreases with the foam content (FC), but the fluidity and strength of the FCPB increase first and then decrease with the FC. In addition, the microstructure analysis explains the enhanced strength of FCPB by adding foam. These results contribute to further understanding the effect of foam content on the fluidity and strength of the FCPB.

Keywords

• foam-cemented paste backfill
• foam content
• fluidity
• unconfined compressive strength
• scanning electron microscopy