Journal of Advanced Dielectrics (Dec 2015)
Study the structural and magnetic properties of rare-earth ions (La and Gd) doped Ba0.9575Ca0.0025Ti0.80685Mn0.002475Nb0.002475Zr0.1782O3 (BCTMNZ) ceramics
Abstract
In this paper, we investigated the influence of rare earth (RE=La and Gd) doped Ba0.9575RE0.04Ca0.0025Ti0.80685 Mn0.002475Nb0.002475Zr0.1782O3 (BCTMNZ) ceramics were fabricated by using a conventional solid-state reaction method. The doping effects of La and Gd on the structural and magnetic properties were studied. The structural pattern of the ceramic samples were investigated by X-ray diffraction and the results indicated that both samples shows an orthorhombic structure with pure phase. Strain and crystalline size values for Gd and La doped were 0.31–0.33% and 0.154–0.181μm, respectively. The room temperature hysteresis loops were obtained by using a vibrating sample magnetometer. La doped ceramic showed the higher value of magnetization i.e., 0.369μB/f.u. as compared to Gd doped BLTMNZ ceramics.