Strain localisation and failure at twin-boundary complexions in nickel-based superalloys

Abstract

Coherent twin boundaries in nickel-based superalloys are vulnerable sites for alloy failure in demanding environments. Here, the authors show that the abnormal γ″ precipitation mechanism at twin boundaries is responsible for pronounced strain localisation and subsequent failure.