Preparation of Side-By-Side Bicomponent Fibers Using Bio Polyol Based Thermoplastic Polyurethane (TPU) and TPU/Polylactic Acid Blends

Abstract

In this study, side-by-side bicomponent fibers were prepared by melt spinning using bio-based thermoplastic polyurethane (TPU) and TPU/polylactic acid (PLA) blends. The morphology, thermal and mechanical properties of the fibers were investigated. To this end, the synthesis of TPU using biomass-based polyols and the preparation of TPU/PLA blends were preceded. Their morphological and structural characteristics were investigated. The synthesis of TPU was confirmed through Fourier transform infrared analysis, and as a result of gel permeation chromatograph analysis, a compound having a weight average molecular weight of 196,107 was synthesized. The TPU/PLA blends were blended in the ratio of 80/20, 60/40, 40/60, and 20/80 through a melt extruder. They formed a sea–island structure as a result of scanning electron microscope analysis, and an increase in the PLA content in the TPU matrix caused a decrease in the melt flow index. Finally, TPU/(TPU/PLA) side-by-side bicomponent fibers were prepared by utilizing the above two materials. These fibers exhibited tensile strengths of up to 3624 MPa, with improved biocarbon content of up to 71.5%. These results demonstrate the potential of TPU/(TPU/PLA) side-by-side bicomponent fibers for various applications.

Keywords

• bio-based polyester polyols
• thermoplastic polyurethane
• polylactic acid
• side-by-side bicomponent fiber
• melt spinning