The Effects of Using Different Adhesive on the Thickness Swelling Ratio of LVL Produced from Scotch Pine

Abstract

Most wood properties are affected by changes in moisture content below the wood fiber saturation point. In this study, the thickness swelling ratios of laminated veneer lumber (LVL) produced from Scotch pine (Pinus sylvestris L.) bonded by using polyvinyl acetate (PVAc), polymeric diphenyl methane diisocyanate (pMDI), and a mixture of them were evaluated. Thickness swelling of the samples was calculated after different waiting times under water. While the lowest thickness swelling ratio (1.65%) was determined from bonding with PVAc 92%- pMDI 8%, for 2 hours, the highest thickness swelling ratio (6.35%) was observed from bonding with PVAc 98%- pMDI 2% adhesive for 96 hours. As a result, adding pMDI to the PVAc adhesive reduced the rate of swelling of the test specimens. For this reason, the material can be used potentially in wet or humid places.

Keywords

• scotch pine
• thickness swelling
• adhesives
• lvl
• swelling ratio