Effects of Recrystallization on Tensile Anisotropic Properties for IN738LC Fabricated by Laser Powder Bed Fusion

Abstract

This study demonstrates the effects of recrystallization on tensile properties and the anisotropy of IN738LC, a typical γ’ precipitation-strengthened alloy, at both room and high temperatures via the laser powder bed fusion process. The nonrecrystallized columnar microstructure, subjected to standard IN738LC heat treatment up to 1120 °C, and the almost fully recrystallized microstructure, heat-treated at 1204 °C, were compared. The tensile properties strongly depend on whether recrystallization was completed as well as the tensile direction. This can be explained by microstructure characterization, featuring the Taylor factor in the tensile direction, average grain size estimated by ellipse approximation, and the relationship between the grain shape and tensile direction. The shape of the recrystallized grains and the distribution of coarse MC carbides inside the recrystallized grains were determined by the microstructure in an as-built state. In high-temperature tensile tests conducted in the horizontal direction, the separation of the columnar grains caused a brittle fracture. In contrast, dimples were observed at the fracture surface after recrystallization, indicating scope for further improvement in ductility.

Keywords

• laser powder bed fusion
• IN738LC
• heat treatment
• recrystallization
• MC carbide
• anisotropy