Crack Control in Additive Manufacturing by Leveraging Process Parameters and Lattice Design

Abstract

This study investigates the design of additive manufacturing for controlled crack propagation using process parameters and lattice structures. We examine two lattice types—octet-truss (OT) and diamond (DM)—fabricated via powder bed fusion with Ti-6Al-4V. Lattice structures are designed with varying densities (10%, 30%, and 50%) and process using two different laser energies. Using additive-manufactured specimens, Charpy impact tests are conducted to evaluate the fracture behavior and impact energy levels of the specimens. Results show that the type of the lattice structures, the density of the lattice structures, and laser energy significantly influence crack propagation patterns and impact energy. OT exhibits straighter crack paths, while DM demonstrates more random fracture patterns. Higher-density lattices and increased laser energy generally improve the impact energy. DM consistently outperformed OT in the impact energy for angle specimens, while OT showed superior performance in stair specimens. Finally, a case study demonstrates the potential for combining OT and DM structures to guide crack propagation along predetermined paths, offering a novel approach to protect critical components during product failure.

Keywords

• additive manufacturing
• crack propagation
• lattice structures
• impact energy