In Vitro Biofilm Formation on Zirconia Implant Surfaces Treated with Femtosecond and Nanosecond Lasers

Abstract

(1) Background: The purpose of this study was to evaluate how a zirconia implant surface treated with laser technology affects the degree of biofilm formation. (2) Methods: Experimental titanium (Ti) disks were produced that were sandblasted with large grit and acid-etched (T), and they were compared with zirconia (ZrO2) discs with a machined (M) surface topography; a hydrophilic surface topography with a femtosecond laser (HF); and a hydrophobic surface topography with a nanosecond laser (HN) (N = 12 per surface group). An in vitro three-species biofilm sample (Aggregatibacter actinomycetemcomitans (Aa), Porphyromonas gingivalis (Pg), Prevotella intermedia (Pi)) was applied to each disc type, and bacterial adhesion was assessed after 48 and 72 h of incubation using an anaerobic flow chamber model. Statistical significance was determined using the Kruskal–Wallis H test, with Bonferroni correction used for the post-hoc test (α = 0.05). (3) Results: Compared to the T group, the M group exhibited more than twice as many viable bacterial counts in the three-species biofilm samples (p p p p < 0.05). (4) Conclusions: The surface treatment method for zirconia discs greatly influences biofilm formation. Notably, hydrophobic surface treatment using a nanosecond laser was particularly effective at inhibiting Pg growth.

Keywords

• zirconia dental implant
• femtosecond laser
• nanosecond laser
• biofilm formation