Effect of Ce on the Microstructure and Corrosion Resistance of Al-5Mg-3Zn-1Cu Alloy

Abstract

The effects of different Ce content on the microstructure and corrosion resistance of Al-5Mg-3Zn-1Cu alloy in metal mold gravity casting were studied in this paper. The microstructure of the alloy was characterized by scanning electron microscope (SEM) and X-Ray diffractometer (XRD). The corrosivity of all alloys in 3.5 wt.%NaCl solution was studied by electrochemical and immersion corrosion techniques. The results show that the microstructure of the alloy is mainly composed of α-Al, T phase, and Al2Cu phase. Ce can refine the organization of the alloy, but when the addition of Ce is higher than 0.25 wt.%, a massive Ce-rich phase appears in the alloy. The results of a potential polarization test show that the corrosion potential of the alloy increases obviously from −1.253 V to −1.193 V with the increase in Ce content in the alloy.