Influence of Utilization of Natural Waste Fibers Pyrolysis on Mechanical Properties and Microstructure of Concrete

Abstract

The main purpose of this paper is to investigate the impact of the thermal processing of natural fibers on the strength of what is considered fiber-reinforced concrete. Natural fibers extracted from palm trees and bamboo residues were collected and pyrolyzed. The investigation of the morphological alterations that occur during the pyrolysis of natural fibers at a temperature of 200°C showed the impact of the cementitious environment on this process. In addition, the mechanical characteristics of fiber-reinforced concrete were conducted on different dosages (1, 1.5, 2, and 5% wt.) of treated and untreated palm oil, date kernel, and bamboo fibers. The results demonstrated that the inclusion of fibers up to 1.5% wt. enhanced the concrete mixes mechanical properties, which included pyrolyzed fibers. Analyzes of the concrete microstructure revealed that the treated fibers were not damaged. The 1.5% wt. addition of fibers after pyrolysis process can effectively improve their adhesion to the matrix and reduce the width and number of cracks. The analysis of variance results for flexural strength indicated that all sources had no significant impact on the flexural strength of untreated or pyrolysis treated natural fiber reinforced concrete.

Keywords

• Natural fiber
• pyrolysis treatment
• compressive strength
• flexural strength
• splitting tensile strength
• microstructure