Frontiers in Materials (Oct 2021)

Mechanical Properties of Barchip Polypropylene Fibre-reinforced Lightweight Concrete Made With Recycled Crushed Lightweight Expanded Clay Aggregate

  • Ming Kun Yew,
  • Ming Chian Yew,
  • Jing Han Beh,
  • Lip Huat Saw,
  • Foo Wei Lee,
  • Yee Ling Lee

DOI
https://doi.org/10.3389/fmats.2021.753619
Journal volume & issue
Vol. 8

Abstract

Read online

Concrete is one of the broadly used construction materials in the construction industry. This research intends to recommend the replacement of conventional coarse aggregates with recycled lightweight expanded clay aggregate (LECA) which offers several advantages such as lightweight, low cost, and easy availability. Lightweight concrete (LWC) offers numerous benefits; therefore, many researchers are using lightweight aggregate to produce lightweight structural composites concrete to compensate heavy loads by reducing the concrete self-weight due to lower density of lightweight concrete, improving in thermal properties and fire resistance, saving the cost of transportation and handling of precast units in the site. Different percentages (0, 0.15, 0.30, and 0.45%) of volume fraction of barchip polypropylene (BPP) fibre have been incorporated to improve the mechanical properties of lightweight aggregate concrete (LWA) concrete. In this study, the mixture of crushed lightweight expanded clay aggregate (CLECA) and barchip polypropylene (BPP) fibre have been used to achieve compressive strength between 28 and 37 MPa at 28-days with an oven-dry density ranged between 1900 and 2000 kg/m3. It is found that the inclusion of BPP fibres at an optimum volume fraction concrete enhances the compressive strength, splitting tensile strength and modulus of rupture. The compressive strength of the lightweight aggregate concrete containing 0.45% volume fraction of BPP fibre (CLLWAC-BPP0.45%) had achieved the highest compressive strength of 37 MPa at 28-days with a significant increment of about 31% compared to plain concrete. Hence, the findings of this research showed that the development of eco-friendly lightweight structural composites can be used as an alternative solution for conventional lightweight concrete, infrastructure and marine fields application.

Keywords