Effect of the Functionalization of Porous Silicon/WO3 Nanorods with Pd Nanoparticles and Their Enhanced NO2-Sensing Performance at Room Temperature

Abstract

The decoration of noble metal nanoparticles (NPs) on the surface of metal oxide semiconductors to enhance material characteristics and gas-sensing performance has recently attracted increasing attention from researchers worldwide. Here, we have synthesized porous silicon (PS)/WO3 nanorods (NRs) functionalized with Pd NPs to enhance NO2 gas-sensing performance. PS was first prepared using electrochemical methods and worked as a substrate. WO3 NRs were synthesized by thermally oxidizing W film on the PS substrate. Pd NPs were decorated on the surface of WO3 NRs via in-situ reduction of the Pd complex solution by using Pluronic P123 as the reducing agent. The gas-sensing characteristics were tested at different gas concentrations and different temperatures ranging from room temperature to 200 °C. Results revealed that, compared with bare PS/WO3 NRs and Si/WO3 NRs functionalized with Pd NPs, the Pd-decorated PS/WO3 NRs exhibited higher and quicker responses to NO2, with a detection concentration as low as 0.25 ppm and a maximum response at room temperature. The gas-sensing mechanism was also investigated and is discussed in detail. The high surface area to volume ratio of PS and the reaction-absorption mechanism can be explained the enhanced sensing performance.

Keywords

• room temperature
• gas sensor
• porous silicon
• Pd nanoparticles
• WO3 nanorods