Study on the Preventive Effect of Au/CeO₂ on Lithium-Ion Battery Thermal Runaway Caused by Overcharging

Abstract

In this study, a flower-like Au/CeO2 supported catalyst composite anode was prepared to explore its impact on thermal runaway triggered by overcharging and flame. Through structural and performance characterization, it was found that the catalyst has a high specific surface area and good CO catalytic oxidation capability, with a CO removal rate higher than 99.97% at room temperature. Through electrical performance testing, it was discovered that, compared to batteries without the catalyst, batteries using the composite anode did not exhibit significant capacity degradation. In overcharge testing, the catalyst prolonged the voltage rise time and peak voltage occurrence time of the battery. In thermal runaway testing, the addition of the catalyst delayed the detection time of CO and significantly reduced the concentration of thermal runaway products, especially the peak concentration and integrated concentration of CO, demonstrating its effectiveness in reducing thermal runaway products. Therefore, this study provides a new approach for improving the safety of lithium-ion batteries. The catalyst exhibits good performance in reducing toxic gases generated after thermal runaway and delaying the occurrence of thermal runaway, providing strong support for the safe application of lithium-ion batteries.

Keywords

• supported Au/CeO₂ catalyst
• lithium-ion battery
• overcharging
• thermal runaway prevention