Journal of Asian Ceramic Societies (Jul 2023)
Synthesis, densification, and cation inversion in high entropy (Co,Cu,Mg,Ni,Zn)Al2O4 spinel
Abstract
ABSTRACTThe synthesis, densification behavior, and crystallographic site occupancy were investigated for four different spinel-based ceramics, including a high-entropy spinel (Co0.2Cu0.2Mg0.2Ni0.2 Zn0.2)Al2O4. Each composition was reacted to form a single phase, but analysis of X-ray diffraction patterns revealed differences in cation site occupancy with the high-entropy spinel being nearly fully normal. Densification behavior was investigated and showed that fully dense ceramics could be produced by hot pressing at temperatures as low as 1375°C for all compositions. Vickers’ hardness values were at least 10 GPa for all compositions. The cations present in the high-entropy spinel appear to have a stabilizing effect that led to nearly normal site occupancy compared to full cation inversion behavior of nickel aluminate spinel. This is the first report that compares cation site occupancy of a high-entropy spinel to conventional spinel ceramics.
Keywords