Processing of yttrium aluminosilicate (YAS) glasses for dental composites Processamento de vidros de aluminosilicatos de ítrio (YAS) para compósitos odontológicos
Abstract
Two series of silicate glasses were processed to micron-size, sub-micron size, and nanoparticles using three different milling systems: ball milling, attrition, and high-energy milling. The effect of milling time and media size on particle size and contamination were investigated in aqueous and isopropanol suspensions. The particle size was determined using a laser-diffraction particle size analyzer and scanning electron microscopy. The smallest glass particles with a median particle size of 0.3 µm were achieved by a two-step comminution process in a high energy mill.Foram moídas duas séries de vidros silicatos para a obtenção de partículas com dimensões nas faixas micrométrica, submicrométrica e nanométrica, utilizando três tipos distintos de processos de moagem: moagem em moinho de esferas, em atritor, e de alta energia. Foram investigados os efeitos do tempo e do tipo do meio de moagem no tamanho de partícula, em suspensões aquosas e em isopropanol. Foram utilizados um granulômetro com o princípio de difração de laser e um microscópio eletrônico de varredura para a determinação do tamanho de partícula. A distribuição de tamanho de partículas com o menor tamanho médio de partícula igual a 0,3 µm foi obtida para vidros submetidos ao processo de cominuição em duas etapas, utilizando um moinho de alta energia.
Keywords