Crack mechanism and experimental verification on straightening of AZ31B magnesium alloy plate

Abstract

Abstract When plates with edge cracks in the rolling process is straightened by cyclic tensile and compressive stress, the tip of edge crack always accompanied by stress concentration, which leads to crack propagation. In this paper, damage parameters are imported into the plate straightening model based on determining the GTN damage parameters of magnesium alloy materials by inverse finite element calibration method, the influence of different straightening process schemes and prefabricated V-shaped crack geometry on crack growth is analyzed through the way of the combination of simulation and straightening experiment. The results show that the peak values of equivalent stress and equivalent strain under each straightening roll appear at the crack tip. The value of longitudinal stress and equivalent stain decrease with the distance to crack tip becomes larger. The peak value of longitudinal stress appears when the crack circumferential angle is about 100°, and the crack tip is easy to form crack propagation; when the plate passes roll 2 and roll 4, the equivalent stress and strain concentration at the crack tip are most obvious; when the reduction reaches a certain degree, the void volume fraction (VVF) reaches the VVF of the material breaking; with the increase of the entrance reduction, the number of VVF at the crack tip which reaches the material fracture increases, and the length of crack propagation increases; the stress concentration at the tip of V-shaped crack with large length–width ratio is obvious, and the VVF is more likely to reach the VVF at the time of material fracture, crack initiates and propagates easily.