Study on Recovery of Lithium from Lithium-Containing Aluminum Electrolyte

Abstract

The current process of recovering lithium from wasted aluminum electrolyte mostly entails extracting lithium from lithium-containing aluminum electrolyte by acid leaching and dissipation. Aiming at the disadvantages of the existing treatment method, such as the long process flow, environmental pollution, poor working environment, etc., we propose a new technology to extract lithium from the wasted aluminum electrolyte and systematically investigate the effects of raw material particle size, holding time, temperature and other factors on the recovery of lithium. The results show that the better process conditions for the recovery of lithium are as follows: the raw material particle size is 75~150 μm, the additive is CaCl2, the mass ratio of calcium chloride to lithium-containing aluminum electrolyte is 3:5, the reaction temperature is 1473 K, and the holding time is 3 h. After the product of the reaction is crushed and leaching is carried out by using deionized water (pH = 6.8), the temperature of the leaching is 368 K, the leaching time is 3 h, and the solid–liquid ratio is 1/3, and the leaching rate of Li can be up to 75.1%. In addition, the purity of the recovered AlF3 is more than 92.7%. This process realizes the comprehensive and efficient use of lithium-containing aluminum electrolyte and provides a new idea for the development of lithium extraction technology from lithium-containing aluminum electrolyte.

Keywords

• wasted aluminum electrolyte
• secondary resource recovery
• lithium