Comparative Study on the Activity of GaF₃ and Ga₂O₃ Nanoparticle-Doped CsF-AlF₃ Flux for Brazing 6061 Al/Q235 Steel Joints

Abstract

The effect of trace amounts of GaF3 and Ga2O3 nanoparticles on the wettability and spreadability of CsF-AlF3 flux matched Zn-15Al filler metal were comparatively studied on 6061 aluminum alloy and Q235 low-carbon steel. The experimental results indicate that appropriate amounts of GaF3 and Ga2O3 added into the flux could significantly promote the Zn-15Al filler metal to wet and spread on the surface of 6061 aluminum alloy and Q235 low-carbon steel. The optimum ranges for GaF3 and Ga2O3 were 0.0075–0.01wt.% and 0.009–0.01 wt.%, respectively. Comparative analysis showed that the activity of CsF-AlF3 flux bearing GaF3 was higher than that bearing Ga2O3. The reason for this is that the former flux has a stronger ability to remove oxides of the base metal and reduce the interfacial tension of the molten filler metal and the base metal.

Keywords

• spreadability
• wettability
• GaF₃
• Ga₂O₃
• CsF-AlF₃ flux