Boletín de la Sociedad Española de Cerámica y Vidrio (Jun 2000)
Efecto del pH ácido y de la desaireación del medio en el comportamiento frente a la corrosión de la MA 956 preoxidada
Abstract
The lifetime of implants is affected by the aggressivity of the physiological medium, which mainly results from the relatively high concentration of ion chlorides. There are, however, other transient situations that may enhance the aggressivity of the environment in the adjacent zones to the implant. For example, during the first days of the implantation is rather frequent to get bruises, inflammation, and even infections. These modifications could dramatically influence the corrosion behaviour and decrease the life expectancy of the implant. In this work the corrosion behaviour of the MA 956, which has been proposed as a new biomaterial, is investigated under experimental conditions of low pH and deareation, which simulate the most typical medical complications in service.<br><br>Además del contenido en iones cloruro que ya hacen del medio fisiológico un entorno corrosivo, en la vida de un implante se producen situaciones transitorias que pueden provocar cambios locales del medio en torno al implante. En los primeros días de la implantación de un biomaterial es relativamente frecuente que se produzcan hematomas, con bajada en el valor del pH, inflamación e incluso infección. Estas situaciones químicas cambiantes, aunque en general son transitorias pueden modificar drásticamente el comportamiento a corrosión de un biomaterial y por tanto afectar negativamente a la vida en servicio de las prótesis. En este trabajo se presenta el comportamiento a corrosión de la superaleación MA 956 con capa de alúmina, en suero fisiológico, en condiciones de bajo pH y desaireación para simular la posibilidad de hematomas, inflamación e infección de los tejidos que rodean la prótesis, dado que esta superaleación está propuesta como nuevo biomaterial.