Caracterización eléctrica de disoluciones sólidas (Cr,V,Ti)O<sub>2</sub> con estructura rutilo
Abstract
In this work (Cr,V,Ti)O2 solid solutions with rich-TiO2 compositions have been synthesized. Green samples and samples after each calcination have been characterized by X-Ray diffraction at room temperature, UV-V spectroscopy and electronic microscopy, in order to confirm the stability of these solid solutions with rutile-type structure at high temperatures (1400ºC). With the calcined samples at 1400ºC pellets were presses and Seebeck coefficient and complex impedance spectroscopy measurements were done. In these materials, the electrical behaviour corresponds to a extrinsic p-type semiconduction. The electrical conductivity is higher than that obtained in V-TiO2 solid solutions and it is enhanced with the amount of dopants in the TiO2 matrix.En este estudio se han sintetizado disoluciones sólidas (Cr,V,Ti)O2 con composiciones ricas en TiO2. Las muestras, crudas y después de cada calcinación, se han caracterizado a temperatura ambiente por difracción de rayos X, espectroscopia UV-V y microscopía eléctronica para confirmar la estabilidad de estas disoluciones sólidas con estructura rutilo a altas temperaturas (1400 ºC). Se han prensado pastillas con las muestras calcinadas a 1400 ºC y con ellas se han realizado medidas cualitativas del coeficiente de Seebeck y de impedancia compleja. En estos materiales, el comportamiento eléctrico corresponde a semiconducción eléctrica extrínseca tipo-p. La conductividad eléctrica de los mismos es superior a la obtenida en disoluciones sólidas V-TiO2 y aumenta con la cantidad de dopantes introducida en la matriz de TiO2.