Charge-Discharge Properties of the Surface-Modified ZrNi Alloy Electrode with Different Degrees of Boiling Alkaline Treatment

Abstract

Charge-discharge properties of the surface-modified ZrNi negative electrodes with different degrees of boiling alkaline treatment were investigated. The boiling alkaline treatment was performed by immersing the ZrNi electrode in a boiling 6 M KOH aqueous solution for 2 h or 4 h. The initial discharge capacity for the untreated ZrNi negative electrode was 21 mAh·g−1, but it was increased to 114 mAh·g−1 and 308 mAh·g−1 after the boiling alkaline treatments for 2 h and 4 h, respectively. The discharge capacity for the ZrNi negative electrode after the treatment for 2 h steadily increased with repeating charge-discharge cycles as well as that of the untreated electrode, whereas that for the ZrNi negative electrode after the 4 h treatment greatly decreased. The high rate of dischargeability was improved with an increase in the treatment period of time, and the charge-transfer resistance was drastically decreased. Scanning electron microscopy (SEM) and electron dispersive X-ray spectroscopy demonstrated the ZrO2 passive layer on the ZrNi alloy surface was removed by the boiling alkaline treatment to form a porous morphology containing Ni(OH)2, which can be reduced to Ni during charging, leading to the reduction of a barrier for the charge-discharge reactions.

Keywords

• ZrNi
• hydrogen storage alloy
• negative electrode
• nickel-metal hydride (Ni-MH) battery
• boiling alkaline treatment