Journal of Materials Research and Technology (Sep 2023)

Interfacial microstructure, element diffusion, mechanical properties and metallurgical bonding mechanism of 316L-AlSi10Mg multi-material parts fabricated by laser powder bed fusion

  • Huan Miao,
  • Farazila Yusof,
  • Mohd Sayuti Ab Karim,
  • Bo Wu,
  • Sufian Raja,
  • M.Z. Ibrahim,
  • Izhar Aziz,
  • Daolun Chen

Journal volume & issue
Vol. 26
pp. 8351 – 8365

Abstract

Read online

This work explored the interfacial microstructure, element diffusion, mechanical properties and metallurgical bonding mechanism of 316L-AlSi10Mg multi-material parts fabricated by laser powder bed fusion (LPBF). Experimental results revealed that insufficient volumetric energy density (VED) of the laser caused lack-fusion porosity in the 316L-AlSi10Mg transition zone, while too high VED produced keyhole-induced porosity defects. Using the optimal process parameters, multi-material parts can be produced with a good interface metallurgical bonding without significant defects. The partial Fe-FCC phase in 316L stainless steel changed into the Fe-BCC structure, and this shift has also changed the preferred orientation of the grains. The intermetallic compound Al5Fe2 and AlFe phases were found in the transition zone. In addition, Al–Fe icosahedral quasicrystals with five-fold symmetry were found at the boundary of the molten pool, which was caused by an extremely high cooling rate. The tensile strength of 316L-AlSi10Mg specimens is higher than that of AlSi10Mg but lower than that of 316L. In contrast to the 316L and AlSi10Mg regions, the fracture mechanism of multi-material fusion zone exhibits a quasi-cleavage fracture mode. The Vickers microhardness of the Al–Fe interface zone was higher than that of 316L with an average value of 235.57 HV0.2 and AlSi10Mg with 124.59 HV0.2, and the interfacial maximum hardness reached 526.68 HV0.2, which was caused by the very hard intermetallic compound Al5Fe2 and AlFe. The metallurgical bonding mechanism of multi-materials was that the dissimilar metals were mixed and in-situ alloyed in the molten pool by the Marangoni convection-induced strong circular flow during LPBF processing.

Keywords