Nanosized Tungsten Powder Synthesized Using the Nitridation–Decomposition Method

Abstract

A facile, one-step nitridation–decomposition method was developed for the synthesis of nanosized tungsten powder with a high surface area. This approach involved the nitridation of WO3 in NH3 to form mesoporous tungsten nitride (W2N), followed by in situ decomposition of W2N to directly yield single-phase W particles. The phase and morphology evolution during the synthesis were systematically investigated and compared with the carbothermal reduction of WO3. It was revealed that powdered tungsten product with single-phase particles was obtained after nitridation at 800 °C combined with in situ decomposition at 1000 °C, displaying an average particle size of 15 nm and a large specific surface area of 6.52 m2/g. Furthermore, the proposed method avoided the limitations associated with intermediate phase formation and coarsening observed in carbothermal reduction, which resulted in the growth of W particles up to ~4.4 μm in size. This work demonstrates the potential of the nitridation–decomposition approach for the scalable and efficient synthesis of high-quality, fine-grained tungsten powder.

Keywords

• nanosized tungsten powder
• powder processing
• morphology evolution
• in situ synthesis