Study on the Influence of Casing Surface Morphology on the Plugging Performance of Downhole CO₂ Plugging with Sn58Bi

Abstract

Aimed at the problem of gas flurries in carbon dioxide (CO2) geologic sequestration in the wellbore, this paper proposes a sealing method in which the downhole casing is processed with threaded grooves and then plugged with a low-melting-point alloy plug. Based on this method, a small-scale experimental setup was developed for alloy plug molding and gas sealing in this study. Molding and gas sealing experiments with Sn58Bi alloy plugs inside casings with different surface morphologies were carried out. The gas leakage pathway was determined. The microstructure of the interface between the alloy plug and casing was analyzed using an optical microscope. The influence of the inner surface roughness, threaded groove, length-to-diameter ratio, and ambient temperature on the gas sealing performance of the alloy plugs was analyzed. The experimental results show that, with an increase in ambient temperature, the gas sealing performance of the casing increases significantly; when the inner surface of the casing is processed through threaded grooves, the gas sealing performance is better than with smooth hole casing; the gas sealing performance of the alloy plug presents an obvious linear positive correlation with their length-to-diameter ratio. This research provides theoretical support for downhole CO2 plugging using Sn58Bi in the casing.

Keywords

• carbon capture
• utilization and storage
• surface morphology
• Sn58Bi
• gas sealing
• length-to-diameter ratio