Selective Laser Melting of 60NiTi Alloy with Superior Wear Resistance

Abstract

In this work, the selective laser melting (SLM) 60NiTi alloy was successfully fabricated. Through designing an orthogonal experiment of parameters optimization including laser power (P) and scanning speed (v), the optimal parameters window with both high forming quality and appropriate composition proportion was established. The SLM 60NiTi can exhibit high relative density (>98%) and low Ni loss (3. The optimally-selected SLM 60NiTi exhibits a high compression strength of 2.2 GPa and large reversible strain of 7% due to the reversible stress-induced martensitic transformation of the NiTi phase and the large elastic strain of the Ni4Ti3 phase. It also exhibits superior wear resistance to conventional casting solution treated 60NiTi because the NiTi phase formed in an SLM repeated thermal cycle possesses a lower solution Ni atom and thus lower critical stress for martensitic transformation, and is more prone to undergo martensitic transformation upon friction and wear.

Keywords

• 60NiTi alloy
• additive manufacturing
• selective laser melting
• process optimization
• wear resistance