Effect of Mechanical Activation on the Kinetics of Copper Leaching from Copper Sulfide (CuS)

Abstract

The effect of mechanical activation on the copper leaching of copper sulfide, CuS, in 1 M HNO3 (slurry density: 10 g/L) was investigated by analysis of the leachability and the apparent activation energy. Mechanical activation produced an increase in the leachability and a decrease of the activation energy in this leaching reaction. The leachability increased proportionally to the degree of mechanical activation, reaching 96.6% leaching within 60 min at 80 °C from CuS ground at 700 rpm for 15 min. This leaching process was controlled by surface chemical reaction following the shrinking-core model. The apparent activation energy of leaching for CuS (71.5 kJ/mol) in the range of 50 to 80 °C decreased with an increase of the degree of mechanical activation, reaching 44.3 kJ/mol for Cu leaching from CuS ground at 700 rpm for 15 min.

Keywords

• mechanical activation (MA)
• leaching
• copper sulfide
• shrinking-core model
• apparent activation energy