Effect of Mg–Ti Treatment on Nucleation Mechanism of TiN Inclusions and Ferrite

Abstract

Large sizes of columnar crystals and TiN particles have a great influence on the surface quality of ferritic stainless steel. In the present paper, this study proposed to obtain fine-grained equiaxed structures by Mg–Ti treatment. Through the experiment happened in resistance furnace with argon protection, the refining effect of Mg–Ti addition on the microstructure and TiN particles were investigated, and the refinement mechanism was discussed from interface coherence theory. It was found that due to adding Mg and Ti into molten ferritic stainless steel, the equiaxed crystal ratio increased from 37% to 50%, and the size of TiN particles reduced at the same time. The lattice matching characteristics of MgAl2O4/TiN and TiN/δ-Fe were investigated by FIB-HRTEM. According to Bramfitt’s equation, the lattice misfit for (400)MgAl2O4∥(200)TiN and (200)TiN∥(110)δ-Fe was 5.02% and 4.41%, respectively, which were all belong to the effective nucleation range. It could be considered that MgO and MgAl2O4 formed in the molten steel promoted TiN nucleation easier to precipitate out with large quantities in the liquid phase. The TiN particles with more uniform distribution significantly enhanced the heterogenous nucleation of ferritic phase during initial solidification process base on the good lattice fitting condition. Finally the equiaxed crystal ratio of δ-Fe phase increased dramatically.

Keywords

• Mg–Ti treatment
• ferritic stainless steel
• heterogeneous nucleation
• lattice misfit