Reconstructing Kaolinite Compounds for Remarkably Enhanced Adsorption of Congo Red

Abstract

Organic dyes are widely used in many important areas, but they also bring many issues for water pollution. To address the above issues, a reconstructed kaolinite hybrid compound (γ-AlOOH@A-Kaol) was obtained from raw kaolinite (Kaol) in this work. The product was then characterized by X-ray diffraction (XRD), Fourier-transform infrared (ATR-FTIR), Brunauer-Emmett-Teller (BET), and scanning electron microscopy (SEM), and the absorption properties of γ-AlOOH@A-Kaol for congo red were further studied. The results demonstrated that flower-like γ-AlOOH with nanolamellae were uniformly loaded on the surface of acid-treated Kaol with a porous structure (A-Kaol). In addition, the surface area (36.5 m2/g), pore volume (0.146 cm3/g), and pore size (13.0 nm) of γ-AlOOH@A-Kaol were different from those of A-Kaol (127.4 m2/g, 0.127 cm3/g, and 4.28 nm, respectively) and γ-AlOOH (34.1 m2/g, 0.315 cm3/g, and 21.5 nm, respectively). The unique structure could significantly enhance the sorption capacity for congo red, which could exceed 1000 mg/g. The reasons may be ascribed to the abundant groups of -OH, large specific surface area, and porous structure of γ-AlOOH@A-Kaol. This work provides an efficient route for comprehensive utilization and production of Kaol-based compound materials that could be used in the field of environmental conservation.

Keywords

• kaolinite
• adsorbent
• congo red
• reconstruct