Impact of Laser Ablation Strategies on Electrochemical Performances of 3D Batteries Containing Aqueous Acid Processed Li(Ni_0.6Mn_0.2Co_0.2)O₂ Cathodes with High Mass Loading

Abstract

Lithium-ion batteries are currently one of the most important energy storage devices for various applications. However, it remains a great challenge to achieve both high energy density and high-power density while reducing the production costs. Cells with three-dimensional electrodes realized by laser ablation are proven to have enhanced electrochemical performance compared to those with conventional two-dimensional electrodes, especially at fast charging/discharging. Nevertheless, laser structuring of electrodes is still limited in terms of achievable processing speed, and the upscaling of the laser structuring process is of great importance to gain a high technology readiness level. In the presented research, the impact of different laser structuring strategies on the electro-chemical performance was investigated on aqueous processed Li(Ni0.6Mn0.2Co0.2)O2 cathodes with acid addition during the slurry mixing process. Rate capability analyses of cells with laser structured aqueous processed electrodes exhibited enhanced performance with capacity increases of up to 60 mAh/g at high current density, while a 65% decrease in ionic resistance was observed for cells with laser structured electrodes. In addition, pouch cells with laser structured acid-added electrodes maintained 29–38% higher cell capacity after 500 cycles and their end-of-life was extended by a factor of about 4 in contrast to the reference cells with two-dimensional electrodes containing common organic solvent processed polyvinylidene fluoride binder.

Keywords

• laser ablation
• 3D battery
• high mass loading
• NMC 622
• aqueous processing
• pouch cells