Carbonated 3D-Printable Polymer Composite for Thermo-Mechanically Stable Applications

Abstract

In this report, we investigate the infusion of carbon dioxide into a 3D-printable photosensitive polymer. The result is a carbonated polymer composite material. In use, polymer composite materials expect to succeed where ordinary polymers and metals fail. This is due to the tailorability of composite materials for specific applications. Usually, micro/nano-particulates are embedded as fillers within a polymer matrix, enhancing the overall material properties. Here, carbon dioxide (CO2) microbubbles serve as the filler within a nylon-like polymer matrix. Additive manufacturing by stereolithography (SLA) of the carbonated polymer composite proved possible using the digital light projection (DLP) 3D printing technique. Post-heat treatment using thermogravimetric analysis of the samples at elevated temperatures resulted in a 33% mass reduction, indicative of nearly complete solvent removal and curing. An initial increase in polymer carbonation duration showed a 16% increase in porosity, more stable thermal profiles, and a 40% decrease in specific heat capacity. Thermo-mechanical compressive tests on an optimal carbonated sample revealed a 70% increase in compressive strength over its neat counterpart and a peak modulus at 50 °C of 60 MPa. Such 3D-printable carbonated polymer composites may find use in applications requiring high strength-to-weight ratio thermally stable polymers and applications requiring a versatile and convenient storage medium for on-demand CO2 deposition or supercritical fluid phase transformation.

Keywords

• thermomechanical properties
• carbonated polymers
• additive manufacturing
• multi-functional composites
• differential scanning calorimetry (DSC)