Experimental investigation and comparison of PBI/MWCNT and PSF/MWCNT membranes for recovering water from RO reject of brackish water by FO

Abstract

The performances of polybenzimidazole (PBI) and polysulfone (PSF) membranes for recovering water from reverse osmosis (RO) reject of brackish water through forward osmosis (FO) were assessed and compared. Non-functionalised multi-walled carbon nanotubes (MWCNT) were added to the membrane casting solutions, with concentrations ranging from 0 to 3 wt%. The experiment was conducted for eight samples using RO reject of brackish water as the feed solution (FS) and 2 M analytical grade MgCl2 as the draw solution (DS). The hydrophilicity, water permeability, salt rejection rate (Rs), water flux (WF) and porosity of the membranes improved with increasing MWCNT content up to 2 wt%. Also, the structural parameter, salt permeability and reverse solute flux decreased. PBI/MWCNT2 wt% exhibited the best performance among the membranes tested compared with porosity of 70 ± 4 %, structural parameter of 0.36 ± 0.2 μm, and Rs of 93.5 %. In contrast with the pristine PBI membrane, an average water flux enhancement of 15 % and 49 % was observed for the FS and DS sides, respectively, for PBI/MWCNT2 wt%. It is evident from the results that including MWCNT improves the performance of both membranes, with better relative performance for PBI membranes than PSF membranes.

Keywords

• Polybenzimidazole
• Polysulfone
• Multi-walled carbon nanotubes
• Membranes
• Forward osmosis